TY - JOUR N2 - The melt cleaning is an important aspect in the production of high-quality aluminum castings. Specifically inclusions within the melt and an excessively high hydrogen content lead to defects and undesired porosity in the castings. Although it is possible to reduce the amount of hydrogen and oxidic inclusions by purge gas treatment and the use of melting salts, it is impossible to remove oxides (bifilms) created during filling of gating system. Paper deals with the effects of melt quality and the placement of a filter in the filling system on Al-7%Si-Mg alloy mechanical properties. Three different filters were used: (a) rectangular ceramic pressed filter with 3 mm thickness (b) cubical pressed ceramic filter with thickness 10 mm (c) cubical pressed ceramic filter with thickness 22 mm. The results showed that the highest tensile strength values were obtained from the filter with thickness of 22 mm. Numerical simulation analysis of the filling process showed that velocity reduction by filter is the major phenomenon affecting the mechanical properties. Another evaluated aspect during experiments was capability of filters to retain old bifilms. For this purpose multiply remelted alloy was prepared and analyzed. Results showed that filter efficiency increases with decreasing melt quality as a result of possibility to retain “old” bifilms better than small and thin “new” bifilms. L1 - http://www.czasopisma.pan.pl/Content/113028/PDF/AMM-2019-3-47-Bruna.pdf L2 - http://www.czasopisma.pan.pl/Content/113028 PY - 2019 IS - No 3 EP - 1106 DO - 10.24425/amm.2019.129500 KW - Bifilm KW - numerical simulation KW - reoxidation KW - mechanical properties KW - filtration A1 - Bruna, M. A1 - Remišová, A. A1 - Sládek, A. PB - Institute of Metallurgy and Materials Science of Polish Academy of Sciences PB - Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences VL - vol. 64 DA - 2019.09.03 T1 - Effect of Filter Thickness on Reoxidation and Mechanical Properties of Aluminium Alloy AlSi7Mg0.3 SP - 1100 UR - http://www.czasopisma.pan.pl/dlibra/publication/edition/113028 T2 - Archives of Metallurgy and Materials ER -