@ARTICLE{Mocek_J._Studies_2012, author={Mocek, J. and Chojecki, A.}, number={No 4}, journal={Archives of Foundry Engineering}, howpublished={online}, year={2012}, publisher={The Katowice Branch of the Polish Academy of Sciences}, abstract={In sand moulds, at a distance of 3 mm from the metal- mould interface, the sensors of temperature, and of oxygen and hydrogen content were installed. Temperature and the evolution of partial gas pressure have been analysed in moulds bonded with bentonite with or without the addition of seacoal, water glass or furan resin. Moulds were poured with ductile iron. For comparison, also tests with the grey iron have been executed. It was found that the gas atmosphere near the interface depends mainly on the content of a carbonaceous substance in the mould. In the green sand moulds with 5% of seacoal or bonded with furan resin, after the mould filling, a sudden increase in the hydrogen content and the drop of oxygen is observed. This gas evolution results from the oxidation of carbon and reduction of water vapour in the mould material, and also from the reduction of water vapour and alloy reoxidation. In carbon-free sand, the evolution in the gas composition is slower because water vapour is reduced only at the interface. Changes of oxygen and hydrogen content in the controlled zone are determined by the transport phenomena.}, type={Artykuły / Articles}, title={Studies of Gas Atmosphere Near the Metalmould Interface During Casting and Solidification of Ductile Iron}, URL={http://www.czasopisma.pan.pl/Content/87176/PDF/28_paper.pdf}, doi={10.2478/v10266-012-0126-6}, keywords={Ductile iron, Metal-mould interface, Gas evolution, Surface of castings}, }