@ARTICLE{Rasheed_Mohammad_Zarar_Phase_2021,
 author={Rasheed, Mohammad Zarar and Nam, Sun-Woo and Lee, Sang-Hoon and Park, Sang-Min and Cho, Ju-Young and Kim, Taek-Soo},
 volume={vol. 66},
 number={No 4},
 journal={Archives of Metallurgy and Materials},
 pages={1001-1005},
 howpublished={online},
 year={2021},
 publisher={Institute of Metallurgy and Materials Science of Polish Academy of Sciences},
 publisher={Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences},
 abstract={Liquid Metal Extraction process using molten Mg was carried out to obtain Nd-Mg alloys from Nd based permanent magnets at 900oC for 24 h. with a magnet to magnesium mass ratio of 1:10. Nd was successfully extracted from magnet into Mg resulting in ~4 wt.% Nd-Mg alloy. Nd was recovered from the obtained Nd-Mg alloys based on the difference in their vapor pressures using vacuum distillation. Vacuum distillation experiments were carried out at 800oC under vacuum of 2.67 Pa at various times for the recovery of high purity Nd. Nd having a purity of more than 99% was recovered at distillation time of 120 min and above. The phase transformations of the Nd-Mg alloy during the process, from Mg12Nd to α-Nd, were confirmed as per the phase diagram at different distillation times. Pure Nd was recovered as a result of two step recycling process; Liquid Metal Extraction followed by Vacuum Distillation.},
 type={Article},
 title={Phase Evolution During Extraction and Recovery of Pure Nd from Magnet},
 URL={http://www.czasopisma.pan.pl/Content/119287/PDF/AMM-2021-4-16-Taek-Soo%20Kim.pdf},
 doi={10.24425/amm.2021.136414},
 keywords={Liquid metal extraction, Rare Earth Recycling, Vacuum Distillation, phase transformation},
}