@ARTICLE{Konar_R._Ultrasonic_2017, author={Konar, R. and Mician, M.}, volume={vol. 17}, number={No 2}, journal={Archives of Foundry Engineering}, howpublished={online}, year={2017}, publisher={The Katowice Branch of the Polish Academy of Sciences}, abstract={The article deals with ultrasonic testing possibilities of the copper alloy centrifugal casts. It focused on the problems that arise when testing of castings is made of non-ferrous materials. Most common types of casting defects is dedicated in theoretical introduction of article. Ultrasonic testing technique by conventional ultrasound system is described in the theoretical part too. Practical ultrasonic testing of centrifugal copper alloy cast - brass is in experimental part. The experimental sample was part of centrifugally cast brass ring with dimensions of Ø1200x34 mm. The influence of microstructure on ultrasonic attenuation and limitations in testing due to attenuation is describes in experimental part. Conventional direct single element contact ultrasound probe with frequencies of 5 MHz, 3.5 MHz and 2 MHz were used for all experimental measurements. The results of experimental part of article are recommendations for selecting equipment and accessories for casting testing made of non-ferrous metals.}, type={Artykuły / Articles}, title={Ultrasonic Inspection Techniques Possibilities for Centrifugal Cast Copper Alloy}, URL={http://www.czasopisma.pan.pl/Content/102004/PDF/afe-2017-0047.pdf}, doi={10.1515/afe-2017-0047}, keywords={Non-destructive testing, Centrifugal casts, Ultrasonic attenuation, Copper alloy, Brass microstructure}, }