Hybrid filter material was obtained via modification of polypropylene (PP) nonwoven with nanosize zinc oxide particles of a high aspect ratio. Modification was conducted as a three-step process, a variant of hydrothermal method used for synthesis of nano-ZnO, adopted for coating three dimensional polymeric nonwoven filters. The process consisted of plasma treatment of nonwoven to increase its wettability, deposition of ZnO nanoparticles and low temperature hydrothermal growth of ZnO rods. The modified nonwovens were investigated by a high resolution scanning electron microscopy (HR-SEM). It has been found that the obtained hybrid filters offer a higher filtration efficiency, in particular for so called most penetrating particle sizes.
Methane (CH4) sensitivity of zinc oxide (ZnO) thin film has been studied in the present work. The sensor element comprises
of a chemically fabricated ZnO semiconducting layer and a layer of palladium (Pd) as catalyst. The catalyst layer was formed on the surface of semiconducting ZnO following a wet chemical process from palladium chloride (PdCl2) solution. Fundamental features of a sensor element e.g. sensitivity, response time and recovery process has been studied. The effect of operating temperature on performance of the sensor material has been investigated and a choice of optimum temperature was made at around 200oC. The sensor element exhibited reasonable sensitivity of about 86% at this temperature in presence of 1 vol% methane (CH4) in air.
Constantly developing nanotechnology provides the possibility of manufacturing nanostructured composites with a polymer matrix doped with ceramic nanoparticles, including ZnO. A specific feature of polymers, i.e. ceramic composite materials, is an amelioration in physical properties for polymer matrix and reinforcement. The aim of the paper was to produce thin fibrous composite mats, reinforced with ZnO nanoparticles and a polyvinylpyrrolidone (PVP) matrix obtained by means of the electrospinning process and then examining the influence of the strength of the reinforcement on the morphology and optical properties of the composite nanofibers. The morphology and structure of the fibrous mats was examined by a scanning electron microscope (SEM) with an energy dispersive spectrometer (EDS) and Fourier-transform infrared spectroscopy (FTIR). UV –Vis spectroscopy allowed to examine the impact of zinc oxide on the optical properties of PVP/ZnO nanofibers and to investigate the width of the energy gap.
Experimental investigation was conducted on the thermal performance and pressure drop of a convective cooling loop working with ZnO aqueous nanofluids. The loop was used to cool a flat heater connected to an AC autotransformer. Influence of different operating parameters, such as fluid flow rate and mass concentration of nanofluid on surface temperature of heater, pressure drop, friction factor and overall heat transfer coefficient was investigated and briefly discussed. Results of this study showed that, despite a penalty for pressure drop, ZnO/water nanofluid was a promising coolant for cooling the micro-electronic devices and chipsets. It was also found that there is an optimum for concentration of nanofluid so that the heat transfer coefficient is maximum, which was wt. %=0.3 for ZnO/water used in this research. In addition, presence of nanoparticles enhanced the friction factor and pressure drop as well; however, it is not very significant in comparison with those of registered for the base fluid.
The paper presents investigations of microstructure of varistors of damaged surge arrester counters. A similar ZnO varistor, not subjected before to operation, was a point of reference in this research. The results of investigations of the ZnO varistors show an untypical phase composition of their material, which was characterized by unsatisfying homogeneity and cohesion. The degradation processes of varistor material in the subsequent stages were recognized and described. A harmful impact of humidity inside the untight surge arrester counter on its operation and its ZnO varistors was proved. Some conclusions being the result of the operation checking of surge arrester counters were presented too.
The aim of the present study was to develop a modifier for water glass. The method of thermal generation of metal oxide nanoparticles was adapted and used in the research. Nanoparticles of ZnO from the thermal decomposition of basic zinc carbonate were used. A method for the modifier introduction was developed, and the effect of modifier content and organic solvent type on the physico-chemical properties of binder (viscosity) and quartz wettability was determined. Binder viscosity was examined from the flow curves plotted with the help of a RHEOTEST 2 rotational rheometer equipped with proper software. Quartz wettability was determined examining timerelated changes in the value of the contact angle in a quartz-binder system, until full stabilisation of the angle value has been achieved. Binder modification was carried out on sodium water glass designated as R"145". The water glass modifiers were suspensions of ZnO nanoparticles in propanol and methanol at a fixed concentration of c = 0.3 M and with the size of nanoparticles comprised in a range of <61 - 981 nm>. Water glass modification with the suspensions of ZnO nanoparticles in methanol and propanol showed the effect of modifier on the water glass viscosity and quartz wettability. This effect depends on the type of alcohol used. The ZnO suspension in propanol (alcohol with a longer hydrocarbon chain) affects more strongly the viscosity of binder and quartz wettability than the methanol suspension.
The paper presents the results of investigations concerning the application of zinc oxide - a wideband gap semiconductor in optical planar waveguide structures. ZnO is a promising semiconducting material thanks to its attractive optical properties. The investigations were focused on the determination of the technology of depositions and the annealing of ZnO layers concerning their optical properties. Special attention was paid to the determination of characteristics of the refractive index of ZnO layers and their coefficients of spectral transmission within the UV-VIS-NIR range. Besides that, also the mode characteristics and the attenuation coefficients of light in the obtained waveguide structures have been investigated. In the case of planar waveguides, in which the ZnO layers have not been annealed after their deposition, the values of the attenuation coefficient of light modes amount to a~ 30 dB/cm. The ZnO layers deposited on the heated substrate and annealed by rapid thermal annealing in an N2 and O2 atmosphere, are characterized by much lower values of the attenuation coefficients: a~ 3 dB/cm (TE0 and TM0 modes). The ZnO optical waveguides obtained according to our technology are characterized by the lowest values of the attenuation coefficients a encountered in world literature concerning the problem of optical waveguides based on ZnO. Studies have shown that ZnO layers elaborated by us can be used in integrated optic systems, waveguides, optical modulators and light sources.
Single crystalline cesium doped ZnO nanorods with homogeneous size and shape were grown hydrothermally on ITO substrates that are presented in our previous work. According to the previous work, XRD analysis showed that cesium doped ZnO nanorods are wurtzite single crystals and are grown preferentially along the c-axis. Also, the electrical conductivity of doped ZnO showed higher values for the 1% cesium, which confirmed incorporation of the cesium dopant. Cesium doped ZnO nanorods are suitable candidates for applications in solar cells. So, in this research, we employed cesium doped ZnO nanorods with the different dopant concentration in inverted polymer solar cell. By comparing the effect of doped ZnO nanorods with diverse dopant concentration (0, 0.5, 1.0, 1.5 and 2%) on the performance of devices, 1.0% cesium doped ZnO was found as the most effective doping level among the selected doping concentrations. Also, using 1.0% cesium doped ZnO nanorods, Jsc of 8.21 mA/cm², Voc of 0.541V and Fill Factor of 63.01% were achieved, which led to power conversion efficiency of 2.80%.
ZnO thin layers were deposited on p-type silicon substrates by the sol-gel spin-coating method and, then, annealed at various temperatures in the range of 573–873 K. Photoluminescence was carried out in the temperature range of 20–300 K. All samples showed two dominant peaks that have UV emissions from 300 nm to 400 nm and visible emissions from 400 nm to 800 nm. Influence of temperature on morphology and chemical composition of fabricated thin layers was examined by XRD, SEM, FTIR, and Raman spectroscopy. These measurements indicate that ZnO structure is obtained for samples annealed at temperatures above 573 K. It means that below this temperature, the obtained thin films are not pure zinc oxide. Thus, annealing temperature significantly affected crystallinity of the thin films.
This paper presents a review of models of the current transport in different kind of heterojunctions (HJs) and their characteristics. In order to effectively deduce the dominant electron transport for the HJs based on ZnO or Zn1−xMgxO layers grown on Si substrate by MBE a comparison is performed – which type of the HJ exhibits better electrical properties. The current–voltage characteristics for the studied HJs were measured within 280–300 K. The transport properties of the HJs are explained in terms of Anderson model with reference to aforementioned current transport models. It is found, that the mechanisms of current transport for all of the studied HJs are similar. At a low forward voltage bias the tunneling current dominates while at medium voltage bias (0.5–1 V) multitunneling capture-emission prevails with the electron trap located at 0.1–0.25 eV below the bottom of a ZnO (Zn1−xMgxO) conduction band. Beyond this voltage bias space charge limited current governs the current transport.
In this work we discuss a method of preparation of a highly sensitive light detector based on ZnO nanorods. A photoresistor constructed by us is based on a heterojunction between high quality ZnO nanorods and high resistivity p-type Si used as a substrate for nanorods’ deposition. ZnO nanorods are grown by a modified version of a microwave assisted hydrothermal method which allows for growth of high quality ZnO nanorods in a few minutes. The obtained photoresistor responds to a wide spectral range of light starting from near infrared (IR) to ultraviolet (UV). Properties of the detector are evaluated. We propose the use of the detector as an optical switch.
This paper demonstrates the use of a zinc oxide (ZnO) thin film in a 1-μm ring laser cavity as a saturable absorber to successfully generate Q-switching pulses. The tunability of the laser pulses is achieved by integrating a tunable bandpass filter (TBPF) in an ytterbium-doped laser cavity that results in 9.4 nm of tuning range, which wavelength is from 1040.70 nm to 1050.1 nm. The peak energy in the pulse which is 1.47 nJ was measured together with a minimum pulse width of 2.4 μs. In addition, the repetition rate increases from 25.77 to 45.94 kHz as the pump power level being increased from 103.1 to 175.1 mW. The results obtained in this experiment demonstrated consistent results and stable throughout the experiment. Therefore, ZnO thin film is considered as a good candidate in 1-μm pulsed laser applications.
A laboratory study was performed to study the effects of various operating factors, viz. adsorbent dose, contact time, solution pH, stirring speed, initial concentration and temperature on the adsorption of triphenyltin chloride (TPT) onto coal fly ash supported nZnO (CFAZ). The adsorption capacity increases with increase in the adsorbent amount, contact time, pH, stirring speed and initial TPT concentration, and decrease with increase in the solution temperature. The adsorption data have been analyzed by Langmuir, Freundlich, Temkin and Dubinin-Radushkevich (D-R) adsorption models to determine the mechanistic parameters associated with the adsorption process while the kinetic data were analyzed by pseudo first-order, pseudo second-order, Elovich, fractional power and intraparticle diffusivity kinetic models. The thermodynamic parameters of the process were also determined. The results of this study show that 0.5 g of CFAZ was able to remove up to 99.60% of TPT from contaminated natural seawater at 60 min contact time, stirring speed of 200 rpm and at a pH of 8. It was also found that the equilibrium and kinetic data fitted better to Freundlich and pseudo second-order models, respectively. It can therefore be concluded that CFAZ can be effectively used for shipyard process wastewater treatment
High-power terahertz sources operating at room-temperature are promising for many applications such as explosive materials detection, non-invasive medical imaging, and high speed telecommunication. Here we report the results of a simulation study, which shows the significantly improved performance of room-temperature terahertz quantum cascade lasers (THz QCLs) based on a ZnMgO/ZnO material system employing a 2-well design scheme with variable barrier heights and a delta-doped injector well. We found that by varying and optimizing constituent layer widths and doping level of the injector well, high power performance of THz QCLs can be achieved at room temperature: optical gain and radiation frequency is varied from 108 cm−1 @ 2.18 THz to 300 cm−1 @ 4.96 THz. These results show that among II–VI compounds the ZnMgO/ZnO material system is optimally suited for high-performance room-temperature THz QCLs.
Transparent Al doped ZnO nanocrystalline films with a crystallite size less than 19 nm are obtained by spray pyrolysis. Band gap increases monotonically from 3.16 to 3.31 eV with increasing aluminum dopant up to 1.56 at.% facilitating increasing width of a transmission window in addition to the band gap tuning of 4.74% which compares favorably well with literature. UV emission with continuously increasing intensity is obtained which reflects on the good crystalline quality of the films. Also the defect emissions are suppressed remarkably as the dopant Al concentration increases in ZnO. The band gap tuning by quite small increment in dopant amount makes the present films, much attractive for the fabrication of light emitting devices with a much sought-for benefit of large area fabrication. FESEM shows the surface is granular with grain size lying in the range of 20–35 nm and EDX confirms the presence of Al in the doped samples.