To investigate the mechanical properties of tunnel lining concrete under different moderate-low strain rates after high temperatures, uniaxial compression tests in association with ultrasonic tests were performed. Test results show that the ultrasonic wave velocity and mass loss of concrete specimen begin to sharply drop after high temperatures of 600°C and 400°C, respectively, at the strain rates of 10‒5s‒1 to 10‒2s‒1. The compressive strength and elastic modulus of specimen increase with increasing strain rate after the same temperature, but it is difficult to obtain an evident change law of peak strain with increasing strain rate. The compressive strength of concrete specimen decreases first, and then increases, but decreases again in the temperatures ranging from room temperature to 800°C at the strain rates of 10‒5s‒1 to 10‒2s‒1. It can be observed that the strain-rate sensitivity of compressive strength of specimen increases with increasing temperature. In addition, the peak strain also increases but the elastic modulus decreases substantially with increasing temperature under the same strain rate.
The impacts of industrial wastewater contamination on the geotechnical properties of clayey soil have been studied in the research presented in this paper. The contaminant in question is industrial wastewater released from Thi-Qar oil refinery as a by-product of production, and the soil samples obtained from Thi-Qar oil refinery plant in Al-Nassyriah (a city located in the south of Iraq). The geotechnical properties of contaminated soil samples were compared with those of intact soil to measure the effects of such a contaminant. The soil samples were obtained from three locations in the study area; representing the highly contaminated area, the slightly contaminated area, and the intact area used as a reference for comparison of test results. The results of the tests showed that the contaminant causes an increase of natural moisture content, field unit weight, Atterberg’s limits, and maximum dry unit weight, as well as an increase of the compression index and the coefficient of vertical consolidation. Also, the contaminant causes a decrease in specific gravity, the optimum moisture content initial void ratio, the swelling index, the coefficient of permeability, and cohesion between soil particles.
The transitional siliceous rocks from the Belchatow lignite deposit belong to the deposits with heterogeneous petrographic composition. The research allows us to identify among others, opoka-rocks and gaizes. The mineralogical-chemical analysis proves that the main ingredients of the studied rocks commonly used as building material are minerals of the SiO₂ group. Laboratory tests show that the nature of siliceous mineral phases has several effects on the geomechanical parameters of the studied transitional rocks. They are a reduction in water content and rock porosity, which leads to the transition of opal type A to opal type crystobalit and trydymit and then to quartz or microquartz. Their density and strength parameters are increased.
Heating of steel or structural aluminum alloys at a speed of 2 to 50 K/min – characterizing the fire conditions – leads to a reduction in mechanical properties of the analyzed alloys. The limit of proportionality fp, real fy and proof f₀₂ yield limit, breaking strength fu and longitudinal limit of elasticity E decrease as the temperature increases. Quantitative evaluation of the thermal conversion in strengths of structural alloys is published in Eurocodes 3 and 9, in the form of dimensionless graphs depicting reduction coefficients and selected (tabulated) discrete values of mechanical properties. The author’s proposal for an analytical formulation of code curves describing thermal reduction of elasticity modulus and strengths of structural alloys recommended for an application in building structures is presented in this paper.
Magnesium alloys thanks to their high specific strength have an extensive potential of the use in a number of industrial applications. The most important of them is the automobile industry in particular. Here it is possible to use this group of materials for great numbers of parts from elements in the car interior (steering wheels, seats, etc.), through exterior parts (wheels particularly of sporting models), up to driving (engine blocks) and gearbox mechanisms themselves. But the use of these alloys in the engine structure has its limitations as these parts are highly thermally stressed. But the commonly used magnesium alloys show rather fast decrease of strength properties with growing temperature of stressing them. This work is aimed at studying this properties both of alloys commonly used (of the Mg-Al-Zn, Mn type), and of that ones used in industrial manufacture in a limited extent (Mg-Al-Sr). These thermomechanical properties are further on complemented with the microstructure analysis with the aim of checking the metallurgical interventions (an effect of inoculation). From the studied materials the test castings were made from which the test bars for the tensile test were subsequently prepared. This test took place within the temperature range of 20°C – 300°C. Achieved results are summarized in the concluding part of the contribution.
Crystals of PbTiO3 and 0.9PbTiO3-0.1(Na0.5Bi0.5)TiO3 were obtained by the flux growth method whereas crystals of (Na0.5Bi0.5)TiO3 were growth by the Czochralski method. Raman spectroscopy and polarized light microscopy were performed at room temperature. The Raman spectra of 0.9PbTiO3-0.1(Na0.5Bi0.5)TiO3 shown significant changes comparing to the base materials PbTiO3 and (Na0.5Bi0.5)TiO3. A domain structure was investigated by use polarized light microscopy. Dielectric permittivity measurements were carried out in the temperature range from 20°C to 550°C and a frequency from 1 kHz to 1 MHz. These showed higher dielectric permittivity for the crystals 0.9PbTiO3-0.1(Na0.5Bi0.5)TiO3 than the source materials PbTiO3 and (Na0.5Bi0.5)TiO3.
The high value of dielectric constant makes it possible to applied 0.9PbTiO3-0.1(Na0.5Bi0.5)TiO3 as efficient dielectric medium in a capacitors. The small size of the domain structure with the easy possibility of switching by application of an external electric field, give opportunities to apply these materials to FRAM memory applications. Moreover, the high sensitivity of these materials to the surrounding gases e.g. ammonia, chlorine, hydrogen, etc., allows the construction of sensor devices.
Natural gas is a mixture of 21 components and it is widely used in industries and homes. Knowledge of its thermodynamic properties is essential for designing appropriate processes and equipment. This paper presents simple but precise correlations of how to compute important thermodynamic properties of natural gas. As measuring natural gas composition is costly and may not be effective for real time process, the correlations are developed based on measurable real time properties. The real time properties are temperature, pressure and specific gravity of the natural gas. Calculations with these correlations are compared with measured values. The validations show that the average absolute percent deviation (AAPD) for compressibility factor calculations is 0.674%, for density is 2.55%, for Joule-Thomson coefficient is 4.16%. Furthermore, in this work, new correlations are presented for computing thermal properties of natural gas such as enthalpy, internal energy and entropy. Due to the lack of experimental data for these properties, the validation is done for pure methane. The validation shows that AAPD is 1.31%, 1.56% and 0.4% for enthalpy, internal energy and entropy respectively. The comparisons show that the correlations could predict natural gas properties with an error that is acceptable for most engineering applications.
Among the copper based alloys, Cu-Al-X bronzes are commonly used as mold materials due to their superior physical and chemical properties. Mold materials suffer from both wear and corrosion, thus, it is necessary to know which one of the competitive phenomenon is dominant during the service conditions. In this study, tribo-corrosion behavior of CuAl10Ni5Fe4 and CuAl14Fe4Mn2Co alloys were studied and electrochemical measurements were carried out using three electrode system in 3.5 % NaCl solution in order to evaluate their corrosion resistance. In tribo-corrosion tests, alloys were tested against zirconia ball in 3.5 % NaCl solution, under 10N load with 0.04 m/s sliding speed during 300 and 600 m. The results indicate that (i) CuAl10Ni5Fe4 alloy is more resistant to NaCl solution compared to CuAl14Fe4Mn2Co alloy that has major galvanic cells within its matrix, (ii) although CuAl10Ni5Fe4 alloy has lower coefficient of friction value, it suffers from wear under dry sliding conditions, (iii) as the sliding distance increases, corrosion products on CuAl14Fe4Mn2Co surface increase at a higher rate compared to CuAl10Ni5Fe4 leading to a decrease in volume loss due to the lubricant effect of copper oxides.
The investigation results of the influence of the reclaim additions on the properties of moulding sands with the GEOPOL geopolymer
binder developed by the SAND TEAM Company were presented. Two brands of hardeners were applied in the tested compositions, the
first one was developed by the SAND TEAM Company, marked SA72 and the new hardener offered by the KRATOS Company, marked
KR72. The main purpose of investigations was to determine the influence of reclaim fractions and the applied hardener on the basic
moulding sands properties, such as: bending and tensile strength, permeability and grindability. The unfavourable influence of the reclaim
additions into moulding sands on the tested properties as well as an increased hardening rate, were found. Moulding sands, in which the
hardener KR72 of the KRATOS Company was used, were less sensitive to the reclaim additions.
The results of investigations of moulding sands with an inorganic binder called GEOPOL, developed by the SAND TEAM Company are
presented in the paper. Hardeners of various hardening rates are used for moulding sands with this binder. The main aim of investigations
was determination of the influence of the hardening rate of moulding sands with the GEOPOL binder on technological properties of these
sands (bending strength, tensile strength, permeability and grindability). In addition, the final strength of moulding sands of the selected
compositions was determined by two methods: by splitting strength and shear strength measurements. No essential influence of the
hardening rate on such parameters as: permeability, grindability and final strength was found. However, the sand in which the slowest
hardener (SA 72) were used, after 1 hour of holding, had the tensile and bending strength practically zero. Thus, the time needed for taking
to pieces the mould made of such moulding sand will be 1.5 - 2 hours.
The present study, aims to investigate the effect of minor Zr and Nb alloying on soft magnetic and electrical properties of Fe86(ZrxNb1-x)7B6Cu1 (x = 1, 0.75, 0.5, 0.25) alloys. The investigated alloys were prepared through the melt spinning process. Within the examined compositional range (Nb up to 5.25at%, respectively), the soft magnetic properties and electrical resistivity of the alloys continuously increase with increasing Nb content. However increasing the Nb content further decreases such properties. We could confirm the influence of ratio of Zr and Nb on grain growth and crystallization fraction during crystallization by using the soft magnetic properties and electrical properties.
Studies were carried out to determine the effect of heat treatment parameters on the plastic properties of unalloyed ausferritic ductile iron,
such as the elongation and toughness at ambient temperature and at – 60 °C. The effect of austenitizing temperature (850, 900 and 950°C)
and ausferritizing time (5 - 180 min.) at a temperature of 360°C was also discussed. The next step covered investigations of
a relationship that is believed to exist between the temperature (270, 300, 330, 360 and 390 °C) and time (5, 10, 30, 60, 90, 120, 150, 180,
240 min.) of the austempering treatment and the mechanical properties of unalloyed ausferritic ductile iron, when the austenitizing
temperature is 950°C. The “process window” was calculated for the ADI characterized by high toughness corresponding to the EN-GJS800-10-RT
and EN-GJS-900-8 grades according to EN-PN 1564 and to other high-strength grades included in this standard. Low-alloyed
cast iron with the nodular graphite is an excellent starting material for the technological design of all the ausferritic ductile iron grades
included in the PN-EN-1624 standard. The examined cast iron is characterized by high mechanical properties stable within the entire range
of heat treatment parameters.
A series of copper oxide thin films were synthesized through direct current magnetron sputtering on glass and silicon substrates with various process parameters. Initially, optical microscopy images and their histograms were analyzed to determine the optical quality of the obtained layers and then histograms were created using Image Histogram Generator software. Next, the morphology, and cross-section and layer composition of the samples were evaluated. Finally, the transmission spectra of the thin films were recorded. Transmittance and reflection spectra of the UV–vis analysis were utilized to calculate the optical band gap, the extinction coefficient, and the absorption coefficient of the oxidized layers. Samples showed low transmittance (up to 40%) in the region of 400 to 1000 nm. The mean absorption coefficient varied from ~3 · 105 to ~6 · 105 1/cm and from ~2 · 105 to ~4 · 105 1/cm in the region of 2 eV to 3.5 eV. The extinction coefficient ranged from 0 to 0.11 in the region from 300 to 3000 nm. Reflectance of the samples was ~20% in the region of 1000 to 2500 nm and ranged from 20%-50% in the region of 1000 to 3000 nm. We verified the process parameters of the Cu2O structure to improve the quality as a buffer layer. On the basis of this preliminary analysis, we propose the most promising and future-oriented solutions in photovoltaic applications.
The results presented in this article are part of the research on fatigue life of various foundry alloys carried out in recent years in the Lukasiewicz Research Network – Institute of Precision Mechanics and AGH University of Science and Technology, Faculty of Foundry Engineering. The article discusses the test results obtained for the EN-GJS-600-3 cast iron in an original modified low-cycle fatigue test (MLCF), which seems to be a beneficial research tool allowing its users to evaluate the mechanical properties of materials with microstructural heterogeneities under both static and dynamic loads. For a comprehensive analysis of the mechanical behaviour with a focus on fatigue life of alloys, an original modified low cycle fatigue method (MLCF) adapted to the actually available test machine was used. The results of metallographic examinations carried out by light microscopy were also presented. From the analysis of the results of the conducted mechanical tests and structural examinations it follows that the MLCF method is fully applicable in a quick and economically justified assessment of the quality of ductile iron after normalizing treatment.
Properties of excitons confined to potential fluctuations due to indium distribution in the wetting layer which accompany self-assembled InAs/GaAs quantum dots are reviewed. Spectroscopic studies are summarized including time-resolved photoluminescence and corresponding single-photon emission correlation measurements. The identification of charge states of excitons is presented which is based on results of a theoretical analysis of interactions between the involved carriers. The effect of the dots’ environment on their optical spectra is also shown.
This article presents the results of laboratory tests of the physical and mechanical properties of various types of sandstone selected from ten quarries from Carpathian flysch. The parameters were used to evaluate the quality of the sandstone and its suitability for use as armourstone in accordance with applicable standards and quality guidelines. The requirements of the BN-79/8952-31, EN 13383-1:2003 and the CIRIA, CUR, CETMEF (2007) standards were compared. Sandstone can display a large variability of parameters depending on its origin. This, in turn, results in a varying degree of its susceptibility to the destructive effects of water and climate.