The study investigates the effect of the organic compound representing the cellulose derivative - sodium salt of carboxymethyl cellulose (CMC/Na) on the structure of the main component of bentonite (B) - montmorillonite (MMT). Structural analysis revealed that the CMC/Na of different viscosity interacts with the mineral only via surface adsorption, causing at the same time partial or full delamination of its layered structure. This was confirmed by the XRD diffraction tests. Such polymer destructive influence on the structure of the modified main component of the bentonite limits the use of its composites as an independent binder in moulding sand technology, but does not exclude it from acting as an additive being a lustrous carbon carrier. According to the IR spectra of the B/CMC/Na materials, it can be stated that the interaction between the organic and inorganic parts is based on the formation of hydrogen bonds. That kind of the interpretation applies especially to the MMT modified in the bentonite with a lower viscosity polymer. The characteristics of the main IR absorption bands for composites with a higher viscosity polymer indicates the formation of less stable structures suggesting the random nature of the hydrogen bonds formation.
The intercalation into interlayer spaces of montmorillonite (MMT), obtained from natural calcium bentonite, was investigated. Modification of MMT was performed by the poly(acrylic acid-co-maleic acid) sodium salt (co-MA/AA). Efficiency of modification of MMT by sodium salt co-MA/AA was assessed by the infrared spectroscopic methods (FTIR), X-ray diffraction method (XRD) and spectrophotometry UV-Vis. It was found, that MMT can be relatively simply modified with omitting the preliminary organofilisation – by introducing hydrogel chains of maleic acid-acrylic acid copolymer in a form of sodium salt into interlayer galleries. A successful intercalation by sodium salt of the above mentioned copolymer was confirmed by the powder X-ray diffraction (shifting the reflex(001) originated from the montmorillonite phase indicating an increase of interlayer distances) as well as by the infrared spectroscopy (occurring of vibrations characteristic for the introduced organic macromolecules). The performed modification causes an increase of the ion exchange ability which allows to assume that the developed hybrid composite: MMT-/maleic acid-acrylic acid copolymer (MMT-co- MA/AA) can find the application as a binding material in the moulding sands technology. In addition, modified montmorillonites indicate an increased ability for ion exchanges at higher temperatures (TG-DTG, UV-Vis). MMT modified by sodium salt of maleic acid-acrylic acid copolymer indicates a significant shifting of the loss of the ion exchange ability in the direction of the higher temperature range (500–700°C).
A determination of the heating degree of the moulding sand with bentonite on the grounds of simulating investigations with the application of the MAGMA program, constitutes the contents of the paper. To this end the numerical simulation of the temperature distribution in the virtual casting mould was performed. It was assumed that the mould cavity was filled with a moulding sand with bentonite of a moisture content 3,2 % and bentonite content 8 %. A computer simulation can be used for predicting the heating degree of moulding sands with bentonite. Thus, prediction of the active bentonite (montmorillonite) content in individual layers of the overheated moulding sand can be done by means of the simulation. An overheating degree of a moulding sand with bentonite, and thus the bentonite deactivation depends on a temperature of a casting alloy, casting mass, ratio of: masssand : masscasting, moulding sand amount in the mould and contact area: metal – mould (geometry of the casting shape). Generally it can be stated, that the bentonite deactivation degree depends on two main factors: temperature of moulding sand heating and time of its operation.
Bentonites and clays are included in the group of drilling fluids materials. The raw materials are mainly clay minerals, which are divided into several groups, like montmorillonite, kaolinite, illite, biotite, muscovite, nontronite, anorthoclase, microcline, sanidine or rutile, differing in chemical composition and crystal lattice structure. Clay minerals have a layered structure forming sheet units. The layers merge into sheets that build up to form the structure of the mineral.
The aim of the studies carried out in the ŁUKASIEWICZ Research Network - Foundry Research Institute is to explore the possibility of using minerals coming from Polish deposits.
The article outlines the basic properties of hybrid bentonites, which are a mixture of bentonite clay called beidellite, originating from overburden deposits of the Turoszów Mine, and foundry bentonite from one of the Slovak deposits. As part of the physico-chemical tests of minerals, measurements included in the PN-85/H-11003 standard, i.e. montmorillonite content, water content and swelling index, were carried out. Additionally, the loss on ignition and pH chemical reaction were determined. Based on the thermal analysis of raw materials, carried out in the temperature range from 0 to 1000oC, changes occurring in these materials during heating, i.e. thermal stability in contact with liquid metal, were determined.
Examinations of the sand mixture based on pure clay and bentonite and of the sand mixture based on hybrid bentonites enabled tracing changes in permeability, compressive strength and tensile strength in the transformation zone as well as compactability referred to the clay content in sand mixture. Selected technological and strength parameters of synthetic sands are crucial for the foundry, because they significantly affect the quality of the finished casting.
Based on the analysis of the results, the optimal composition of hybrid bentonite was selected.