Usually porous metals are known as relatively excellent characteristic such as large surface area, light, lower heat capacity, high toughness and permeability for exhaust gas filter, hydrogen reformer catalyst support. The Ni alloys have high corrosion resistance, heat resistance and chemical stability for high temperature applications. In this study, the Ni-based porous metals have been developed with Hastelloy powder by gas atomization and water atomization in order to find the effects of powder shape on porous metal. Each Hastelloy powder is pressed on disk shape of 2 mm thickness with 12 tons using uniaxial press machine. The specimens are sintered at various temperatures in high vacuum condition. The pore properties were evaluated using Porometer and microstructures were observed with SEM.
Porous metals show not only extremely low density, but also excellent physical, mechanical and acoustic properties. In this study, Hastelloy powders prepared by gas atomization are used to manufacture 3D geometries of Hastelloy porous metal with above 90% porosity using electrostatic powder coating process. In order to control pore size and porosity, foam is sintered at 1200~1300°C and different powder coating amount. The pore properties are evaluated using SEM and Archimedes method. As powder coating amount and sintering temperature increased, porosity is decreased from 96.4 to 94.4%. And foam density is increased from 0.323 to 0.497 g/cm3 and pore size is decreased from 98 to 560 μm. When the sintering temperature is increased, foam thickness and strut thickness are decreased from 9.85 to 8.13mm and from 366 to 292 μm.
A mechanistic exposure experiment was performed on the commercially available and welded Ni-Cr-Mo-Fe alloy samples used in the piping materials of the coal gasification pilot plant. Thermodynamic Ellingham-Pourbaix stability diagrams were constructed to provide insight into the mechanism of the observed corrosion behavior. The thermodynamic inference on the corrosion mechanism was supplemented with the morphological, compositional and microstructural analyses of the exposed samples using scanning electron microscopy, X-ray diffraction and energy-dispersive X-ray spectroscopy analyses. X-ray diffraction result revealed stable corrosion products of NiO, MoNi4 and Cr4.6MoNi2.1 after accumulated total exposure duration of 139 h to the corrosive atmosphere. Scanning electron microscopy and energy-dispersive X-ray spectroscopy positively identified formation of rather continuous and adherent pre-oxidation corrosion products although extensively peeled-off oxides were finally observed as corrosion scales on the post-exposure alloy samples, which were attributed to the chlorination/oxidation into thin (spalled) oxides.