The five-layer Aurivillius type structures with the general chemical formula Bi5Fe2-xMnxTi3O18, where x = 0, 0.6, 1.2 have been synthesized and tested. The SEM studies showed a significant increase in grain size in the manganese-modified Aurivillius type ceramic material (for x = 1.2). The increase in the amount of manganese ions (Mn3+) affects the decrease in the temperature at which the relaxation processes take place. Namely from 525 K (1 kHz) and 725 K (1 MHz) for BFT sample (x = 0) to 355 K (1 kHz) and 565 K (1 MHz) for BFM12T sample (x = 1.2). Using the Arrhenius’s law and the Vogel-Fulcher’s relationship the activation energy (Ea) and the relaxation time have been calculated. The value of Ea increases with the increase of the Mn amount from 0.737 eV (for x = 0) to 0.915 eV (for x = 1.2).

Multiferroic six-layer Aurivillius type Bi7Fe3Ti3O21 ceramics was obtained by conventional mixed oxides method. The final sintering process was taken in several different sintering times, which determined changes in properties of discussed ceramic material. The structure and dielectric properties of the material are reported. In order to examine the technological conditions on the crystal structure, XRD analysis was carried out. The microstructure, as well as the quantitative and qualitative analysis of the chemical composition were investigated by scanning electron microscope with an energy dispersion spectrometer. The main purpose of the paper is to present the effect of sintering time on the microstructure, crystallographic structure and dielectric properties of Bi7Fe3Ti3O21 ceramics.