The paper presents the problem which concerning the technology of bimetallic castings in materials configuration: high-chromium steel as the working layer and grey cast iron as the base part. The aim of the studies was integrate the process of manufacturing of bimetallic casting with the heat treatment of hardening type of X46Cr13 steel insert by applying the mould with sandmix on a matrix of chromite sand. Range of studies included the chemical composition analysis, non-destructive ultrasonic tests to examine the quality of the permanent bond between the working layer (steel insert) and the base part (grey cast iron) of the bimetallic castings, hardness measurements as well as metallographic examinations performed on the optical and scanning electron microscopes. On the basis of obtained results was concluded that the self-hardening process occurred in the X46Cr 13 steel working layer and in result of this the hardness on its surface equalled approx. 45HRC in case of the bimetallic castings with full permanent bond between both parts.
The paper presents the technology of manufacturing layered castings, consisting of grey cast iron (base part) and high-chromium stainless steel (working part/layer). The aim of researches was an attempt of integration of heat treatment of steel X46Cr13 grade with founding of grey cast iron in bimetallic system and determination of the influence of cooling rate of bimetallic system in classical sand mould with bentonite on microstructure and hardness of the working layer. The castings were manufactured using mould cavity preparation method, where steel plate was poured by grey cast iron using different pouring temperature and thickness of base part. Then, the quality of joint between cast iron and steel plate was estimated by using ultrasonic non-destructive testing. The efficiency of heat treatment process was analysed by measurement of hardness and in metallographic examination. Conducted studies showed, that self-hardening’s ability of steel X46Cr13 let obtain technologically usable layered casting characterized by hardness of working surface up to 35 HRC.