Manganese is an effective element used for the modification of needle intermetallic phases in Al-Si alloy. These particles seriously

degrade mechanical characteristics of the alloy and promote the formation of porosity. By adding manganese the particles are being

excluded in more compact shape of “Chinese script” or skeletal form, which are less initiative to cracks as Al5FeSi phase. In the present

article, AlSi7Mg0.3 aluminium foundry alloy with several manganese content were studied. The alloy was controlled pollution for achieve

higher iron content (about 0.7 wt. % Fe). The manganese were added in amount of 0.2 wt. %, 0.6 wt. %, 1.0 wt. % and 1.4 wt. %. The

influence of the alloying element on the process of crystallization of intermetallic phases were compared to microstructural observations.

The results indicate that increasing manganese content (> 0.2 wt. % Mn) lead to increase the temperature of solidification iron rich phase

(TAl5FeSi) and reduction this particles. The temperature of nucleation Al-Si eutectic increase with higher manganese content also. At

adding 1.4 wt. % Mn grain refinement and skeleton particles were observed.