The paper presents the possibility of the usage of the concfocal microscope for define the type of tribological wear present during the technical dry friction on the testing machine of the pin-on-disc T-01M. The pin was a remelted high-speed steel and the disc was made from sintered carbides. The surface layer of the high-speed steel was remelted with the electric arc with different parameters. The intensity of the electric arc current was changed, the scanning speed and the single, overlapping remeltings were used. On the basis of the 3D, 2D view of the surface friction of the pin (made from the remelted high-speed steel), disc (made from the sintered carbides) and the surface roughness profile run along the marked line, the presence of the abrasive wear can be defined with the description of the elementary wear processes due to the abrasive and/or adhesive wear.

The work presents the results of the research and tests of the surface machining of the S355NL and X5CrNi18-10 steels with the concentraded stream of heat with the usage of the GTAW method. The surface layers of the tested steels were remelted with the electric arc using the current of the electric arc 50, 100, 150 and 200A.The machining was done in the atmosphere of argon with the constant speed of the welding head. A microscope examination was performed of the obtained structure and measurements of depth, width and hardness of the received surface layer were performed. Moreover the relation between the current of the electric arc and geometry of the remelted layers with their microhardness was examined.