The article presents the results of investigations performed on segregation of elements in the billets. The research were performed under standard industrial conditions, during high carbon steel production cycle. Probes (templates with the thickness of 20 mm) were taken from billets with square cross-section of 160 mm. Segregation of elements was determined based on the quantitative analysis of results performed by using spark spectrometry pursuant to PN-H-04045. Changes in concentrations of elements were analysed along two cross-sections. Element contents were performed at points distanced from each other by approx. 10 mm. The segregation of carbon, sulphur and phosphorus was determined for different billets.

The article provides results of the microstructure examinations and mechanical properties (hardness and microhardness tests) of the welded joint T91 steel taken from the live steam pipeline. Examined joint has been exploited for about 45 000 hours in a temperature of 535oC and the steam pressure equals to 13.5 MPa. Examined joint was made as a double bead by the additional materials with a different chemical composition. It was proved that the joint was characterized by a differential microstructure on the cross-section of the weld. Moreover, decarburized zone in the lower alloyed material and carbides zone in the higher alloyed material were revealed in the weld line and on the boundary penetration of beads. Furthermore, it was shown that the main mechanism of a joint degradation is a privileged precipitation of carbides on the grain boundaries, and an increase of their size.

The application of hardfacing is one of the ways to restore the functional properties of worn elements. The possibility of using filler materials rich in chrome allows for better wear resistance than base materials used so far. The paper presents the results of research on the use of 3 different grades of covered electrodes for the regeneration of worn track staves. The content of the carbon in the covered electrodes was from 0,5% to 7% and the chromium from 5% to 33%. The microscopic and hardness tests revealed large differences in the structure and properties of the welds. The differences in the hardness of the welds between the materials used were up to 150 HV units. The difference in wear resistance, in the ASTM G65 test, between the best and worst materials was almost 12 times big.