The article describes the detection of a defect in a cast iron casting. It analyzes the cause of the crack in the Turbine Component casting. In this article, we are focusing on a particular turbine casting that is commonly used in automobiles as one of the components for turbochargers. The turbine is a casting made of ductile cast iron with a visible crack on the naked eye. The formation of cracks in castings is a common but undesirable phenomenon in the foundry practice. It is important to identify the errors, but also to know the cause of defects in castings. The solution is a detailed error analysis. In this paper I used metallographic analysis and magnetic powder method. The crack formation is due to tension in the casting, which results in tensile, shear, or shear forces. The crack formation kinetics is difficult because it is still very low during hardening and shortly after the casting is overloaded. The crack is most often due to core resistance or shrinkage molds that begin after the surface layer is tightened when the strength of the material is negligible to the end of the crystallisation.
The paper deals with the effect of heating of various prepared batch materials into semisolid state with subsequent solidification of the cast under pressure. The investigated material was a subeutectic aluminium alloy AlSi7Mg0.3. The heating temperature to the semisolid was chosen at 50% liquid phase. The used material was prepared in a variety of ways: heat treatment, inoculation and by squeeze casting. Also the influence of the initial state of material on inheritance of mechanical properties and microstructure was observed. The pressure was 100 MPa. Effect on the resulting casting structure, alpha phase distribution and eutectic silicon was observed. By using semisolid squeeze casting process the mechanical properties and microstructures of the casts has changed. The final microstructure of the casts is very similar to the microstructure that can be reached by technology of thixocasting. The mechanical properties by using semisolid squeeze casting has been increased except the heat treated material.