The paper deals with possibility to improve operating performance of cast-iron heat exchangers by providing them with a copper alloy (CuTi2Cr) with the use of the flame spraying method. A test exchanger was cast of a gray cast iron with vermicular graphite in ferriticpearlitic matrix obtained in production conditions at KAW-MET Iron Foundry with the wire method used to vermicularize the material. The test samples were two plates cast in sand molds, of which one was given a flame-sprayed CuTi2Cr coat on one side. The operating performance of such model cast-iron heat exchangers, with and without CuTi2Cr coating, was tested on a set-up for determining the heat flow rate (thermal power) transferred by the heat exchanger to environment. The obtained results indicate that the value of the heat flow rate characterizing the CuTi2Cr-coated cast-iron heat exchanger was by 10% higher compared to the flow rate of heat conveyed to environment by the heat exchanger without coating.

The objective of the study reported in this paper was to determine the effect of structure on thermal power of cast-iron heat exchangers which in this case were furnace chambers constituting the main component of household fireplace-based heating systems and known commonly as fireplace inserts. For the purpose of relevant tests, plate-shaped castings were prepared of gray iron with flake graphite in pearlitic matrix (the material used to date typically for fireplace inserts) as well as similar castings of gray cast iron with vermicular graphite in pearlitic, ferritic-pearlitic, and ferritic matrix. For all the cast iron variants of different structures (graphite precipitate shapes and matrix type), calorimetric measurements were carried out consisting in determining the heat power which is quantity representing the rate of heat transfer to the ambient environment. It has been found that the value of the observed heat power was affected by both the shape of graphite precipitates and the type of alloy matrix. Higher thermal power values characterize plate castings of gray iron with vermicular graphite compared to plates cast of the flake graphite gray iron. In case of plates made of gray cast iron with vermicular graphite, the highest values of thermal power were observed for castings made of iron with ferritic matrix.