The paper discusses a theoretical and an experimental analyses of steel wire drawing in conical drawing dies with a varying length of the die sizing portion. The theoretical analysis was performed in the Drawing 2D, where the wire temperature and drawing stress were determined. The theoretical study was verified by the measurement of drawing force under laboratory conditions and by industrial multi-stage drawing tests carried out under commercial conditions. A relationship has been shown to exist between die sizing portion length and wire temperature and drawing stress.
This research paper shows the influence of a repeated SPD (Severe Plastic Deformation) plastic forming with the DRECE technique (Dual Rolls Equal Channel Extrusion) on hardening of low carbon IF steel. The influence of number of passes through the device on change of mechanical properties, such as tensile strength TS and yield stress YS, of tested steel was tested. The developed method is based on equal channel extrusion with dual rolls and uses a repeated plastic forming to refinement of structure and improve mechanical properties of metal bands [1-2]. For the tested steel the increase of strength properties after the DRECE process was confirmed after the first pass in relation to the initial material. The biggest strain hardening is observed after the fourth pass.
This paper shows results of researches of a structure and mechanical properties of metal sheets of IF steels subjected torecrystallization
annealing. The annealing was held in the scope of the temperature of 600-900°C over 25 min time. The impact of heat treatment on changes of properties and structure of the researches steel has been analysed. During annealing typical processes of rebuilding of the structure deformed as a result of cold deformation in the form of forming new recrystallized grains and their growth were observed. As the temperature of annealing increases the hardness of the material gradually decreases.
Nil strength temperature of 1062°C and nil ductility temperature of 1040°C were experimentally set for CuFe2 alloy. The highest formability at approx. 1020°C is unusable due to massive grain coarsening. The local minimum of ductility around the temperature 910°C is probably due to minor formation of γ-iron. In the forming temperatures interval 650-950°C and strain rate 0.1-10 s–1 the flow stress curves were obtained and after their analysis hot deformation activation energy of 380 kJ·mol–1 was achieved. Peak stress and corresponding peak strain values were mathematically described with good accuracy by equations depending on Zener-Hollomon parameter.