The current study were performed in order to assess the fabrication possibility of the metal-ceramic composites based on nanocrystalline substrates. The influence of the variable time of the high energy ball-milling (10, 30 and 50 h) on the structure, pores morphology and microhardness of Ti/ZrO2 and Ti/Al2O3 compositions was studied. The X-ray diffraction analysis confirmed the composite formation for all milling times and sintering in the case of Ti/ZrO2 system. Decomposition of substrates during milling process of Ti/Al2O3 system was also observed. Additionally, the changes of lattice parameter as a function of milling time were studied. The morphology of powders and the microstructure of the sintered samples were observed by scanning electron microscopy (SEM). Also, analysis of microhardness and pores structure were performed.

The main purpose of this study was to identify the mineral composition of soil sample taken from the upper layer of topsoil. High absorption of chemical substance is a characteristic for humus-organic layer of topsoil. The source of those substance could be a pollutant emitted to the atmosphere by human activity. The research area includes Upper Silesia region, which is the most industrial region of Poland. In the present study, the phase composition of the top soil separates were analyzed by using X-ray diffraction and Mössbauer spectroscopy. X-ray diffraction analysis revealed the presence of seven mineral phases in the material magnetic separated by lower current (quartz, illite, kaolinite, Fe3+ oxides, hematite, magnetite and pyrite). In case of higher current were identified four phases (quartz, muscovite, kaolinite and K0.94 Na0.06(AlSi3O8)). Mössbauer spectroscopy was used for an extensive analysis of iron-containing phases (pyrrhotite, magnetite, aluminosilicate oxides with Fe3+ and kaolinite/Fe2+ silicate).

The Ti15Mo alloy has been studied towards long-term corrosion performance in saline solution at 37°C using electrochemical impedance spectroscopy. The physical and chemical characterization of the material were also investigated. The as-received Ti15Mo alloy exhibits a single β-phase structure. The thickness of single-layer structured oxide presented on its surface is ~4 nm. Impedance measurements revealed that the Ti15Mo alloy is characterized by spontaneous passivation in the solution containing chloride ions and formation of a double-layer structured oxide composed of a dense interlayer being the barrier layer against corrosion and porous outer layer. The thickness of this oxide layer, estimated based on the impedance data increases up to ~6 nm during 78 days of exposure. The observed fall in value of the log|Z|f = 0.01 Hz indicates a decrease in pitting corrosion resistance of Ti15Mo alloy in saline solution along with the immersion time. The detailed EIS study on the kinetics and mechanism of corrosion process and the capacitive behavior of the Ti15Mo electrode | passive layer | saline solution system was based on the concept of equivalent electrical circuit with respect to the physical meaning of the applied circuit elements. Potentiodynamic studies up to 9 V vs. SCE and SEM analysis show no presence of pitting corrosion what indicates that the Ti15Mo alloy is promising biomaterial to long-term medical applications.

An equiatomic multi-component alloy Ni20Ti20Ta20Co20Cu20 (at. %) was obtained using vacuum arc melting. In order to characterize such an alloy, microstructure analysis has been performed using Scanning and Transmission Electron Microscopy, Electron Backscattered Diffraction, X-ray Diffraction and Energy Dispersive X-ray Spectroscopy techniques. Microstructure analysis revealed the presence of one rhombohedral and two cubic phases. Energy Dispersive X-ray Spectroscopy measurements revealed that both observed phases include five chemical elements in the structure. Using Rietveld refinement approach the lattice parameters were refined for the observed phases.

This paper presents the study of microstructure and properties of 8 mol% yttrium stabilized zirconia coating fabricated by Plasma Spray Physical Vapor Deposition technique on commercial pure titanium. The coating was characterized by X-ray diffraction, high resolution scanning electron microscope, profilometer, nanoindentation and nanomachining tests. The X-ray phase analysis exhibit the tetragonal Zr0.935Y0.065O1.968, TiO and α-Ti phases. The Rietveld refinement technique were indicated the changes of crystal structure of the produced coatings. The characteristic structure of columns were observed in High Resolutions Scanning Electron Microscopy. Moreover, the obtained coating had various development of surfaces, thickness was equal to 3.1(1) µm and roughness 0.40(7) µm. Furthermore, the production coatings did not show microcracks, delamination and crumbing. The performed experiment encourages carried out us to tests for osseointegration.

A new NiTi-based multi-component Ni35Ti35Ta10Co10Cu10 (at.%) alloy was obtained by vacuum arc melting. The microstructure of the alloy has been studied using scanning and transmission electron microscopy, backscatter electron diffraction and X-ray diffraction techniques. The performed measurements showed presence of two cubic and one tetragonal phases. Energy dispersive X-ray spectroscopy analysis confirmed that all the observed phases contained all five principal elements.

The paper presents the technology and basic properties of three compositions of lead-free ceramics: (i) (K0.44Na0.52Li0.04)NbO3, (ii) (K0.44Na0.52Li0.04)NbO3+0.5%mol Nd2O3 and (iii) (K0.44Na0.52Li0.04)NbO3+0.5%mol Pr2O3. Powders of the designed compositions based on KNLN were obtained with the classic ceramic technology, as a result of solid phase synthesis, from a mixture of simple oxides and carbonates. The synthesis of ceramic powders was carried out at Ts = 900°C for ts = 4 h, while compaction by free sintering at Tsint = 1100°C for tsint = 2 h.

XRD studies have shown that doping with praseodymium and neodymium promotes the formation of the tetragonal phase in the base composition (K0.44Na0.52Li0.04)NbO3 at lower temperatures. On the other hand, microstructural tests have shown that the admixture of neodymium and praseodymium improves the sinterability of ceramic samples during the technological process; however, the ceramic samples still exhibit high porosity.

A 20 gram batch weight of NiTi alloy, with a nominal equiatomic composition, was produced by mechanical alloying with milling times of 100, 120, and 140 hours. The differential scanning calorimetry was used to analyze the progress of the crystallization process. The X-ray diffraction examined the crystal structure of the alloy at individual crystallization stages. The observation of the powders microstructure and the chemical composition measurement were carried out using a scanning electron microscope equipped with an energy-dispersive detector. After the milling process, the alloy revealed an amorphous-nanocrystalline state. The course of the crystallization process was multi-stage and proceeded at a lower temperature than the pure amorphous state. The applied production parameters and the stage heat treatment allowed to obtain the alloy showing the reversible martensitic transformation with an enthalpy of almost 5 J/g.

Scientists and medics are still searching for new metallic materials that can be used in medicine, e.g., as material for implants. The following article proposes materials based on titanium with vital elements prepared by combined powder metallurgy and arc melting methods. Four compositions of Ti-28Ta-9Nb, Ti-28Ta-19Nb, Ti-28Ta-9Zr and Ti-28Ta-19Zr (wt.%) have been prepared. The tested material was thoroughly analyzed by X-ray diffraction and scanning electron microscopy. Qualitative phase analysis using X-ray diffraction showed the presence of two phases, α' and β titanium. In addition, a microhardness test was conducted, and the material was characterized in terms of corrosion properties. It was found that the corrosion resistance decreases with an increase of the β phase presence.

This work investigated two titanium-based alloys with a constant tantalum content and variable contents of alloy additives – niobium and zirconium. The Ti-30Ta-10Zr-20Nb (wt.%) and Ti-30Ta-20Zr-10Nb (wt.%) alloys were obtained using a combination of powder metallurgy and arc melting methods. The influence of alloying additives on the structure and properties of the Ti-Ta-Nb-Zr system was studied using, among others: X-ray diffraction and scanning electron microscopy. The X-ray diffraction confirmed the single-β-phase structure of both alloys. In addition, the microscopic analysis revealed that a higher amount of zirconium favoured the formation of larger grains. However, the microhardness analysis indicated that the alloy with the higher niobium content had the higher microhardness. Importantly, the in vitro corrosion study revealed that the addition of niobium promoted the better corrosion resistance of the investigated alloy.