The paper presents the results of research on nanocomposite nickel/graphene oxide (Ni / GO) coatings produced by electrochemical reduction method on a steel substrate. Discussed is the method of manufacturing composite coatings with nickel matrix and embedded graphene oxide flakes. For comparative purposes, the studies also included a nanocrystalline Ni coating without embedded graphene oxide flakes. Graphene oxide was characterized by Raman spectroscopy, infrared spectroscopy (FTIR) and transmission (TEM) and scanning (SEM) electron microscopy. Results of studies on the structure of nickel and composite Ni/GO coatings deposited in a bath containing different amount of graphene oxide are presented. The coatings were characterized by scanning electron microscopy, light microscopy, Raman spectroscopy and X-ray diffraction. The adhesion of the prepared coatings to the substrate was examined by the scratch method. The microhardness of the coatings was measured using the Vickers method on perpendicular cross-sections to the surface. Corrosion tests of the coatings were investigated using the potentiodynamic method. The influence of graphene oxide on the structure and properties of composite coatings deposited from baths with different content of graphene oxide was determined.

The results of research on preparations of alloy Ni-B/B composite coatings produced by chemical reduction method on a carbon steel substrate are collected in this paper. The alloy Ni-B coatings were also investigated for comparative purposes. The produced coatings were subjected to a heat treatment process. The boron powder with the particles size below 1 µm was used as the dispersion phase. The structure of the coatings was examined by X-ray diffraction method. Boron powder particles as well as surface morphology and topography were characterized by scanning electron microscopy. The roughness test, microhardness and corrosion resistance by potentiodynamic method and surface wettability tests were carried out. Analysis of the chemical composition by the EDS method showed that the boron powder particles were evenly embedded in the entire volume of the coating. Ni-B/B composite coatings are characterized by higher hardness than alloy Ni-B coatings. As a result of heat treatment, the Ni3B phase crystallized, which increased the hardness of the coating material. The incorporation of boron powder particles and heat treatment reduce the corrosion resistance of coatings. All produced coatings exhibited hydrophobic properties.