This paper presents the results of the static work analysis of laminated veneer lumber (LVL) beams strengthened with carbon fabric sheets (CFRP). Tested specimens were 45mm wide, 100 mm high, and 1700 mm long. Two types of strengthening arrangements were assumed as follows: 1. One layer of sheet bonded to the bottom face; 2. U-shape half-wrapped reinforcement; both sides wrapped to half of the height of the cross-section. The reinforcement ratios were 0.22% and 0.72%, respectively. In both cases, the FRP reinforcement was bonded along the entire span of the element by means of epoxy resin. The reinforcement of the elements resulted in an increase in the bending strength by 30% and 35%, respectively, as well as an increase in the global modulus of elasticity in bending greater than 20% for both configurations (in comparison to the reference elements).

The article discusses the basic issues related to the technology of friction stir welding (FSW). A short description of technology is provided. The following section provides the analysis of effect of technological parameters (tool rotation and welding speed) on the mechanical properties of the prepared joint (strength, ductility, microhardness). In both cases the analysis refers to aluminum alloys (6056 and AA2195-T0). The comparative analysis showed the phenomenon of the increase in weld strength along with the increase in the rotational speed of the tool during welding. Similarly, with the increase in welding speed, an increase in weld strength was observed. Some exceptions have been observed from the above relations, as described in the article. In addition, examples of material hardness distribution in the joint are presented, indicating their lack of symmetry, caused by the rotational movement of the tool. The analyses were performed basing on the literature data.