In this work, in order to obtain breakdown voltage values of the 4H-SiC p-i-n diodes above 1.7kV, three designs have been examined: single-zone junction termination extention (JTE), double-zone JTE and a structure with concentric rings outside each of the areas of the double-zone JTE (space-modulated JTE). The influence of geometry and the level of p-type doping in the JTE area as well as the charge at the interface between the p-type JTE area and the passivation layer on the diode breakdown voltage was studied. The effect of statistical dispersion of drift layer parameters (thickness, doping level) on diodes breakdown voltage with various JTE structures was investigated as well. The obtained results showed that the breakdown volatge values for a diode with single zone JTE are very sensitive both to the dose of JTE area and charge accumulated at the JTE/dielectric interface. The use of a double zone or space-modulated JTE structures allows for obtaining breakdown voltage above 1.7 kV for a much wider range of doping parameters and with better tolerance to positive charge at the JTE/dielectric interface, as well as better tolerance to statistical dispersion of active layer parameters compared to a single zone JTE structure.

Preparation and properties of hierarchically structured porous silica monoliths have been discussed from the viewpoint of their application as continuous microreactors for liquid-phase synthesis of fine chemical in multi kilogram scales. The results of recent topical papers published by two research teams of Institute of Chemical Engineering Polish Academy of Sciences (ICE) and Department of Chemical Engineering and Process Design, Chemical Faculty, Silesian University of Technology (SUT) have been analyzed to specify the governing traits of microreactors. It was concluded that even enhancement factor of 100 in activity, seen in enzyme catalyzed reactions, can be explained by a proportional reduction of its physical constraints, i.e. huge enhancement of external mass transfer and micromixing. It is induced by very chaotic flows of liquid in tens of thousands of waving connected channels of ca. 25–50 mm in diameter, present in the skeleton. The scale of enhancement in the case of less active catalysts was smaller, but still large enough to consider the most practical applications.