A thermo-insulating moulding sand with a binder made of aluminosilicate microspheres with organic binder was subjected to testing. The aim of the analysis was to determine selected technological properties of the developed compounds. Compressive strength, friability and gas permeability were determined. The binder content was changed within a range of 5÷20 wt% with a 5% step. The applied matrix is characterized by good thermo-insulating properties and a small size of grains, while synthetic organic binder has favourable functional properties, among which the most noteworthy are the extended life and setting time, good rheological properties as well as high resistance to chemical agents. The intended use of the compound is the casting of 3D CRS (Composite Reinforced Skeletons), which are characterized by a well-developed heat transfer surface area, good absorption of impact energy, low mass and a target thickness of connectors within a range of 1.5÷3 mm. The construction of 3D CRS castings is an original concept developed by the employees of the Department of Foundry Engineering at the Silesian University of Technology.

This paper presents the problems related to smelting gray and ductile cast iron. Special attention is paid to the metallurgical quality of cast iron. It depends on the type of furnace, charge materials and the special combination of charge, overheating and holding temperature, melting time, modification and spheroidization method. The evaluation of metallurgical quality has been performed by using derivativethermal analysis (DTA). During the smelting process and secondary metallurgy, the ITACA system was used allowing to obtain information on alloy characteristic temperatures (Tliquidus, TeMin, TeMax, Tsolidus), VPS value, recalescence value, IGQ coefficient, nucleation gauge, porosity etc. The results of investigations and calculations are displayed in the form of graphs and dependencies. It has been shown that the derivative-thermal analysis (DTA) is an effective complement of chemical analysis and it has been found that both the increase in temperature and metal holding time have a negative impact on the metallurgical quality of liquid metal. The metallurgical quality can be improved by using proper composition of charge materials and modifiers.