In this paper results of microstructural observations for series of CuZn39Pb2 alloys produced from qualified scraps are presented. The individual alloy melts were differentiated in terms of thermal parameters of continuous casting as well as refining methods and modifications. Structural observations performed by SEM and TEM revealed formation of different types of intermetallic phases including “hard particles”. EDS results show that “hard particles” are enrich in silicon, phosphorus, iron, chromium and nickel elements. Additionally, formation of Al-Fe-Si and Al-Cr in alloy melts was observed as well. It was found that quantity and morphology of intermetallic phases strongly depends upon the chemical composition of raw materials, process parameters, modifiers and refining procedure applied during casting. It was observed that refining process results in very effective refinement of intermetallic phases, whereas modifiers, particularly carbon-based, results in formation of large particles in the microstructure.
The paper presents the research results of the influence of the precipitation hardening on hardness and microstructure of selected Al-Si and Al-Cu alloys obtained as 30 mm ingots in a horizontal continuous casting process. The ingots were heat treated in process of precipitation hardening i.e. supersaturation with subsequent accelerated or natural ageing. Moreover in the range of the study it has been carried out investigations of chemical constitution, microscopic metallographic with use of scanning electron microscope with EDS analysis system, and hardness measurements using the Brinell method. On basis of obtained results it has been concluded that the chemical constitution of the investigated alloys enables to classify them into Al alloys for the plastic deformation as EN AW-AlSi2Mn (alternatively cast alloy EN AC-AlSi2MgTi) and as EN AW-AlCu4MgSi (alternatively cast alloy EN AC-AlCu4MgTi) grades. Moreover in result of applied precipitation hardening has resulted in the precipitation from a supersaturated solid solution of dispersive particles of secondary phases rich in alloying element i.e. Si and Cu respectively. In consequence it has been obtained increase in hardness in case of AlSi2Mn alloy by approximately 30% and in case of AlCu4MgSi alloy by approximately 20% in comparison to the as-cast state of continuous ingots.
Because of excellent properties, similar to natural bone minerals, and variety of possible biomedical applications, hydroxyapatite (HAp) is a valuable compound among the calcium phosphate salts. A number of synthesis routes for producing HAp powders have been reported. Despite this fact, it is important to develop new methods providing precise control over the reaction and having potential to scale-up. The main motivation for the current paper is a view of continuous synthesis methods toward medical application of produced hydroxyapatite, especially in the form of nanoparticles.