An analysis has been carried out of the influence of annealing time at the preheating temperature of 650 °C on the change in hardness and alloy structure of lamellar graphite cast iron in the working as well as in the laboratory conditions. This preheat temperature is common during reclaiming welding of castings with complex shapes. The changes in unalloyed cast iron EN-GJL 200 to EN-GJL 300 according to ISO 1690 standard and cast iron with low amount of elements such as Sn, Cu, Cr, and Mo and their combinations were assessed. It was found that the cast iron of higher strength grades has better hardness and structural stability. Cast iron alloyed with chromium or its combinations has the highest stability. In unalloyed cast iron, a partial degradation of pearlite occurs; in alloyed cast iron the structural changes are not conclusive.
The paper presents results of Ti-addition to High Chromium Cast Iron (HCCI) on the structure and selected mechanical properties. For this study casted two sets of cylinders with dimensions ø20 mm, ø15 mm x 250 mm, for the High Chromium Cast Iron (HCCI) and with the 4% by mass Ti-addition. Melts were performed in the induction furnace crucible capacity of 15 kg. During the heats the cup with installed S type thermocouple was poured to record the cooling curves. The cylinders were subjected to the static bending strength test. Samples for the test microstructure and Rockwell hardness were cut from the cylinders. The study shows that the addition of titanium had an impact on the structure and thus the properties of High Chromium Cast Iron (HCCI). In subsequent studies, through an appropriate choice of chemical composition and proper process control, it is planned to obtain in the structure the titanium carbides TiC and chromium carbides with type (Cr, Fe)7C3.
The paper presents the technology of manufacturing layered castings, consisting of grey cast iron (base part) and high-chromium stainless steel (working part/layer). The aim of researches was an attempt of integration of heat treatment of steel X46Cr13 grade with founding of grey cast iron in bimetallic system and determination of the influence of cooling rate of bimetallic system in classical sand mould with bentonite on microstructure and hardness of the working layer. The castings were manufactured using mould cavity preparation method, where steel plate was poured by grey cast iron using different pouring temperature and thickness of base part. Then, the quality of joint between cast iron and steel plate was estimated by using ultrasonic non-destructive testing. The efficiency of heat treatment process was analysed by measurement of hardness and in metallographic examination. Conducted studies showed, that self-hardening’s ability of steel X46Cr13 let obtain technologically usable layered casting characterized by hardness of working surface up to 35 HRC.
The present work, presented the study of effect of different inoculants on impact toughness in High Chromium Cast Iron. The molds were pouring in industrial conditions and samples were tested in laboratory in Faculty of Foundry Engineering at AGH. Seven samples were tested - one reference sample, three with different addition of Fe-Ti, and three with different addition of Al. The samples were subjected to impact toughness on Charpy hammer and the hardness test. The presented investigations indicate that for the each inoculant there is an optimal addition at which the sample obtained the highest value of impact toughness. For the Fe-Ti it is 0.66% and for Al is 0.17%. Of all the examined inoculants best results were obtained at a dose of 0.66% Fe-Ti. Titanium is a well-known as a good modifier but very interesting results gives the aluminum. Comparing the results obtained for the Fe-Ti and Al can be seen that in the case of aluminum hardness is more stable. The hardness of all samples is around 40-45 HRC, which is not high for this type of cast iron. Therefore, in future studies it is planned to carry out the heat treatment procedure that may improves hardness.
The paper presents an innovative method of creating the layered castings. The innovation relies on application the 3D printing insert obtaining in SLM (selective laser melting) method. This type of scaffold insert made from pure Ti powder, was placed into mould cavity directly before pouring by grey cast iron. In result of used method was obtained grey cast iron casting with surface layer reinforced by titanium carbides. In range of studies were carried out metallographic researches using light microscope and scanning electron microscope, microhardness measurements and abrasive wear resistance. On the basis of obtaining results was stated that there is a possibility of reinforcing surface layer of the grey cast iron casting by using 3D printing scaffold insert in the method of mould cavity preparation. Moreover there was a local increase in hardness and abrasive wear resistance in spite of the precipitation of titanium carbides in surface layer of grey cast iron. While the usable properties of composite surface layer obtained in result of use of the method presented in the paper, strongly depend of dimensions of scaffold insert, mainly parameters Re and Ri.