TY - JOUR N2 - The measurement results concerning the abrasive wear of AlSi11-SiC particles composites are presented in paper. The method of preparing a composite slurry composed of AlSi11 alloy matrix and 10, 20% vol.% of SiC particles, as well as the method of its highpressure die casting was described. Composite slurry was injected into metal mould of cold chamber pressure die cast machine and castings were produced at various values of the piston velocity in the second stage of injection, diverse intensification pressure values, and various injection gate width values. Very good uniform arrangement of SiC particles in volume composite matrix was observed and these results were publicated early in this journal. The kinetics of abrasive wear and correlation with SiC particles arrangement in composite matrix were presented. Better wear resistance of composite was observed in comparison with aluminium alloy. Very strong linear correlation between abrasive wear and particle arrangement was observed. The conclusion gives the analysis and the interpretation of the obtained results. L1 - http://www.czasopisma.pan.pl/Content/88162/PDF/08_paper.pdf L2 - http://www.czasopisma.pan.pl/Content/88162 PY - 2014 IS - No 3 DO - 10.2478/afe-2014-0058 KW - Composites KW - Pressure die casting KW - Tribological properties A1 - Konopka, Z. A1 - Pasieka, A. PB - The Katowice Branch of the Polish Academy of Sciences DA - 2014 T1 - Tribological Properties of AlSi11-SiCp Composite Castings Produced by Pressure Die Casting Method UR - http://www.czasopisma.pan.pl/dlibra/publication/edition/88162 T2 - Archives of Foundry Engineering ER -