TY - JOUR N2 - Wear resistance of TiC-cast steel metal matrix composite has been investigated. Composites were obtained with SHSB method known as SHS synthesis during casting. It has been shown the differences in wear between composite and base cast steel. The Miller slurry machine test were used to determine wear loss of the specimens. The slurry was composed of SiC and water. The worn surface of specimens after test, were studied by SEM. Experimental observation has shown that surface of composite zone is not homogenous and consist the matrix lakes. Microscopic observations revealed the long grooves with SiC particles indented in the base alloy area, and spalling pits in the composite area. Due to the presence of TiC carbides on composite layer, specimens with TiC reinforced cast steel exhibited higher abrasion resistance. The wear of TiC reinforced cast steel mechanism was initially by wearing of soft matrix and in second stage by polishing and spalling of TiC. Summary weight loss after 16hr test was 0,14รท0,23 g for composite specimens and 0,90 g for base steel L1 - http://www.czasopisma.pan.pl/Content/101983/PDF/afe-2017-0026.pdf L2 - http://www.czasopisma.pan.pl/Content/101983 PY - 2017 IS - No 1 DO - 10.1515/afe-2017-0026 KW - Metal matrix composites KW - MMCs KW - Composite casting KW - TiC reinforced cast steel KW - Wear resistance A1 - Sobula, S. A1 - Tokarski, T. A1 - Olejnik, E. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol. 17 DA - 2017 T1 - Wear Resistance of TiC Reinforced Cast Steel Matrix Composite UR - http://www.czasopisma.pan.pl/dlibra/publication/edition/101983 T2 - Archives of Foundry Engineering ER -