@ARTICLE{Soiński_M.S._The_2013, author={Soiński, M.S. and Jakubus, A.}, number={No 3}, journal={Archives of Foundry Engineering}, howpublished={online}, year={2013}, publisher={The Katowice Branch of the Polish Academy of Sciences}, abstract={The influence of aluminium added in amounts of about 1.6%, 2.1%, or 2.8% on the effectiveness of cast iron spheroidization with magnesium was determined. The cast iron was melted and treated with FeSiMg7 master alloy under industrial conditions. The metallographic examinations were performed for the separately cast rods of 20 mm diameter. They included the assessment of the shape of graphite precipitates and of the matrix structure. The results allowed to state that the despheroidizing influence of aluminium (introduced in the above mentioned quantities) is the stronger, the higher is the aluminium content in the alloy. The results of examinations carried out by means of a computer image analyser enabled the quantitative assessment of the considered aluminium addition influence. It was found that the despheroidizing influence of aluminium (up to about 2.8%) yields the crystallization of either the deformed nodular graphite precipitates or vermicular graphite precipitates. None of the examined specimens, however, contained the flake graphite precipitates. The results of examinations confirmed the already known opinion that aluminium widens the range of ferrite crystallization.}, type={Artykuły / Articles}, title={The Influence of Small Amounts of Aluminium on the Effectiveness of Cast Iron Spheroidization with Magnesium}, URL={http://www.czasopisma.pan.pl/Content/87551/PDF/16_paper.pdf}, doi={10.2478/afe-2013-0064}, keywords={Metallography, Aluminium, cast iron, Spheroidization, Graphite precipitates}, }