@ARTICLE{Kaczmar_J.W._Bending_2013, author={Kaczmar, J.W. and Naplocha, K. and Granat, K. and Kurzawa, A. and Grodzka, E. and Samociuk, B.}, number={No 2}, journal={Archives of Foundry Engineering}, howpublished={online}, year={2013}, publisher={The Katowice Branch of the Polish Academy of Sciences}, abstract={Bending strength, thermal and electric conductivity and microstructure examinations of Cu based composite materials reinforced with Saffil alumina fibres are presented. Materials were produced by squeeze casting method applying the designed device and specially elaborated production parameters. Applying infiltration pressure of 90MPa and suitable temperature parameters provided manufacturing of copper based composite materials strengthened with Saffil alumina fibres characterized by the low rest porosity and good fibre-matrix interface. Three point bending tests at temperatures of 25, 100 and 300ºC were performed on specimens reinforced with 10, 15 and 20% of Saffil fibres. Introduced reinforcement effected on the relatively high bending strengths at elevated temperatures. In relation to unreinforced Cu casting strength of composite material Cu – 15vol.% Saffil fibres increase by about 25%, whereas at the highest applied test temperature of 300o C the improvement was almost 100%. Fibres by strengthening of the copper matrix and by transferring loads from the matrix reduce its plastic deformation and hinder the micro-crack developed during bending tests. Decreasing of thermal and electrical conductivity of Cu after incorporating fibres in the matrix are relatively small and these properties can be acceptable for electric and thermal applications.}, type={Artykuły / Articles}, title={Bending Strength and Fracture Investigations of Cu Based Composite Materials Strengthened with δ-Alumina Fibres}, URL={http://www.czasopisma.pan.pl/Content/87395/PDF/11_paper.pdf}, doi={10.2478/afe-2013-0037}, keywords={Metal matrix composites, Copper, δ-alumina fibres, Squeeze casting, bending strength}, }