@ARTICLE{Hajkowski_J._Validation_2017, author={Hajkowski, J. and Roquet, P. and Khamashta, M. and Codina, E. and Ignaszak, Z.}, volume={vol. 17}, number={No 1}, journal={Archives of Foundry Engineering}, howpublished={online}, year={2017}, publisher={The Katowice Branch of the Polish Academy of Sciences}, abstract={The paper presents the results of experimental-simulation tests of expansion-shrinkage phenomena occurring in cast iron castings. The tests were based on the standard test for inspecting the tendency of steel-carbon alloys to create compacted discontinuities of the pipe shrinkage type. The cast alloy was a high-silicone ductile iron of GJS - 600 - 10 grade. The validation regarding correctness of prognoses of the shrinkage defects was applied mostly to the simulation code (system) NovaFlow & Solid CV (NFS CV). The obtained results were referred to the results obtained using the Procast system (macro- and micromodel). The analysis of sensitivity of the modules responsible for predicting the shrinkage discontinuities on selected pre-processing parameters was performed, focusing mostly on critical fractions concerning the feeding flows (mass and capillary) and variation of initial temperature of the alloy in the mould and heat transfer coefficient (HTC) on the casting - chill interface.}, type={Artykuły / Articles}, title={Validation Tests of Prediction Modules of Shrinkage Defects in Cast Iron Sample}, URL={http://www.czasopisma.pan.pl/Content/101968/PDF/afe-2017-0011.pdf}, doi={10.1515/afe-2017-0011}, keywords={porosity, Castings defects, Shrinkage, Ductile cast iron, Validation}, }